Ceramic Liners Wear Resistant Silicon Carbide (SISIC/RBSIC) Wear Lining Plates
Reaction bonded silicon carbide is a multi-phased material typically containing 7-15% silicon metal, some minor amount of unreacted carbon, with the remaining body being SiC. Reaction bonded SiC materials are manufactured utilizing a variety of processes depending on desired final product geometry, configuration, and required tolerances.
Reaction bonded silicon carbide has proven to be an excellent material choice for wear applications such as pipe liners, flow control chokes and larger wear components in the mining as well as other industries. CALSIC RB offers an economical and reliable material option for many applications where the corrosion resistance or wear resistance of CALSIC S (sintered silicon carbide) is not necessary
Typical properties of silicon carbide are:
Excellent thermal shock resistance
Excellent hot strength
Excellent abrasion resistance
Good thermal conductivity
Relatively low coefficient of thermal expansion
Typical applications for silicon carbide are:
Kiln furniture for powder metal and ceramic processing
Kiln components including:
--hearths
--entrance tiles
--skid rails
--muffles
--side walls
--arches
Available Shape and sizes:
Thickness: from 6mm up to 25mm
Regular Shape: SiSiC tiles, SiSiC Pipe tiles, SiSiC Three Links, SiSiC Elbow, SiSiC Cone Cyclone.
Remark: Other sizes and shape are available upon requests.
| Operating Limits | Units | Typical Value | |
| Contents | SiC | % | 90~92 |
| Si | % | 8~10 | |
| Volume Density | g/cm3 | >3.02 | |
| Hardness | HV | kg/mm2 | 2400 |
| Moh's | 9~9.2 | ||
| Indicated Porosity | % | <0.1 | |
| Compressive Strength | Mpa | >2000 | |
| Flexural Strength | 20ºC | Mpa | 260 |
| 1200ºC | Mpa | 280 | |
| Modulus of Elasticity | 20ºC | Gpa | 330 |
| 1200ºC | Gpa | 300 | |
| Fracture Toughness | Mpa. mm1/2 | 3.3 | |
| Coefficient of Thermal Conductivity 1200ºC | W/(m*k) | 45 | |
| Coefficient of Thermal Expansion 1200ºC | K-1*10-6 | 4.5 | |
| Maximum Temperature | ºC | 1380 | |
| Acid & Alkali Corrosion Resistance | Excellent | ||
1.Established in 1997,25 years experience in wear solutions products.
2.Factory is under expanding, the total construction area is 50,000 sqm.
3.ISO9001:2015 certified,over 400 staffs.
4.Three Own-designed production lines, the ball mils are own produced.
The company specializes in the production of HC series wear-resistant ceramic liners(alumina ball, zirconium silicate ball, zirconia toughed alumina ball, zirconium ball), agate ball, polyurethane ball, 92/T95/ZTA wear-resistant ceramic liner (alumina liner, zirconium toughed aluminum composite liner, zirconia plate), three-in-one,Two-in-one vulcanized ceramic runner sheet,ceramic mending compound, ceramic lining cyclone, ceramic lining pipe.
Q: What is your experience in your products?
A: We have 25 years experience in this industry line. We are professional manufacturer in this area.
){kind=link}