Mineral Processing equipment operates in some of the harshest and remote locations. It is crucial to the Mineral Processing industries that this equipment continues to operate efficiently and its lifecycle is maximised to minimise down time. By appropriately protecting equipment from the extreme wear caused by the high speed and flow rates of ore when processed as a slurry ensures better equipment longevity. Slurry is highly abrasive and can not only cause wear damage to wet processing equipment but also with the inclusion of chemicals and heat, there is constant risk of corrosion and dangerous leakage.
Wear Protection ceramic Linings are used throughout Mineral Processing to protect the steel surfaces of equipment from wear and corrosion. They are used on a range of equipment including pipes, tanks, chutes, pumps, flotation cells, thickeners, launders and feed spouts or chutes.
Qimingxing Ceramic Tile Series
Ceramic Mosaic Pieces
Ceramic Pipe Tiles
Ceramic Curved Tiles(with or without holes)
Ceramic Tapered Tiles
Ceramic Cylinders
Steel Lined with Ceramic Tiles
Irregular Ceramic Tiles
Clipping Ceramic Tiles Interlocking Bricks
| Character | 92 | 95 | T95 | 99 | ZTA | ZrO2 |
| Density(g/cm³) | ≥3.6 | ≥3.65 | ≥3.7 | ≥3.83 | ≥4.15 | ≥5.9 |
| Al2O3(%) | ≥92% | ≥95% | ≥95% | ≥99% | ≥75% | / |
| ZrO2 +Y2O3 | / | / | / | / | ≥21% | ≥99.8% |
| Bending Strength(MPa) | ≥220 | ≥250 | ≥300 | ≥330 | ≥400 | ≥800 |
| Compressive Strength (MPa) | ≥1050 | ≥1300 | ≥1600 | ≥1800 | ≥2000 | / |
| Fracture Toughness(MPa.m1/2) | ≥3.2 | ≥3.2 | ≥3.5 | ≥3.5 | ≥5.0 | ≥7.0 |
| Rockwell Hardness HRA | ≥82 | ≥85 | ≥88 | ≥89 | ≥90 | ≥88 |
| Vickers Hardness HV20(MPa) | ≥950 | ≥1000 | ≥1100 | ≥1200 | ≥1400 | ≥1100 |
| Wear Volume(cm³) | ≤0.25 | ≤0.20 | ≤0.15 | ≤0.10 | ≤0.05 | ≤0.05 |
1.Established in 1997,25 years experience in wear solutions products.
2.Factory is under expanding, the total construction area is 50,000 sqm.
3.ISO9001:2015 certified,over350 staffs.
4.Three Own-designed production lines, the ball mils are own produced.
The company specializes in the production of HC series wear-resistant ceramic liners(alumina ball, zirconium silicate ball, zirconia toughed alumina ball, zirconium ball), agate ball, polyurethane ball, 92/T95/ZTA wear-resistant ceramic liner (alumina liner, zirconium toughed aluminum composite liner, zirconia plate), three-in-one,Two-in-one vulcanized ceramic runner sheet,ceramic mending compound, ceramic lining cyclone, ceramic lining pipe.
){kind=link}