Minerals Use Anti-Abrasive Ceramic Coating Wearing Compound

Product Description

Product Description

                       Minerals Use Anti-Abrasive Ceramic Coating Wearing Compound

1Minerals Use Anti-Abrasive Ceramic Coating Wearing Compound

 

Qimingxing's wearing compounds are unique patented epoxy resin systems containing diamond hard ceramic beads that resist sliding abrasion. Directions for use-surface preparataion: Proper surface preparation is critical to the long termm performance of this product.The exact requirements vary with the severity of the application,expected service life, and initial substrate conditions. 1.On all vertical r overhaed applications,tacking welding expanded metal mesh onto the metal substrate is strongly reconnended prior to application of Wearing Compound. 2.Clean,dry,and abrade application surface.The more torough the degree of surface preparation, the better the performance of the application.If possbible,it is recommended that the surface be grit blasted to a Near White Metal(SSPC-SP10/NACE No.2)Standard.For less severe applications,roughening the sureface with hand tools is suirtable.
 
Mixing:

1.Measure 2 parts resin to 1 part hardener by volume or weight on a clean and dry mixing surface and mix together until iniform in color.(If resin and hardener temperatures are 15ºC/60ºF or below,prehead resin only to about 21ºC/90ºF but not to exceed 37ºC/100ºF) 2.Immediately after abrasive blasting,rub a thin layer of material onto the surface to "wet" for good adhesion.)
 
Operation:

1.Apply filly mixed material to the prepared surface. 2.Initially apply the material in a very thin layer to "wet" out the surface and avoid air entrapment. 3.At 25ºC/77ºF,the working time is 30 minutes.Working and solidify time depend on temperature and mass;the higher the temperature,the larger the mass , the faster the solidifying. 4.Functional cure time is 7 houra at 25ºC/77ºF. 5.Caution!Use approved,positive-pressure,supplied-air respirator when welding or torch cutting near cured compound. Use approved self-contained breathing apparatus when burning,welding,or torch cutting indoors near cured compund.Use approved respirator for dests and mists when grinding or machining cured compound. Do not use open flame on compound.See other cautions on Material Safety Data Sheet.

Detailed Photos

 

 

Product Parameters

 

Item	Index
Color	Grey(White Grain)
Density(g/cm3)	2.0
Weight Ratio(A:B)	2:1
Operating time(min)	10~30(can be customized)
Minimum curing time(min)	30
Full curing time(h)	4
Hardness after solidify(Shore D)	100.0
Compressive strength(Mpa)	111.0
Shear strength(Mpa)	32
Working temperature(ºC)	-20~80(Customized for high temperature)

Company Profile

ABOUT QIMINGXING

Qimingxing offer quality wear and Ant- impact ceramics, in combination with our experienced and competent staff, ensure the increased efficiency and service life of all equipments and materials to which they are applied. - Established Ultrafine Energy Efficiency Technology Research Institute - Increase lifespan of wearable parts - New improved technology and products - Minimal downtime to minimize delays in production - Variety of wear combating options available as a one stop solution - Strong focus on product innovation supported by Chinese Academy of Sciences. - Customized application techniques to suite any wear problem

Packaging & Shipping

 

Certifications

 

OTHER HOT SALE

 

FAQ

 

FAQ

Q: What is your experience in your products?
A: We have 22 years experience in this industry line. We are professional manufacturer in this area.
 
Q: What is your MOQ?
A: The MOQ is different as per different products, for example, 1 Ton for ceramic ball.
 
Q: Can you accept small quantity sample order before production?
A: Yes, we can offer sample for your testing first.

Q: Can you provide free sample?
A: Yes, within 1kg.
 
Q: What is your production time?
A: We have large stock for standard products. Normally within 7-10days after receipt the deposit.
 
Q: What are your payment terms?
A: T/T, L/C, Western Union