Anti Impact Resistant Rubber Composite Plate for Mineral Wear -Resistant Engineering
Product Description
Rubber wear liner size: 500*500*31mm
Ceramic size:147*97*50mm
Weight: 21 kg/piece
|
92 Alumina Ceramic Liners |
WEAR PLATE BACKING MATERIALS |
Mild Steel Backing Plate |
Al2O3:≥92%
Density:≥3.6g/cm³
Porosity:<0.25
compressive strength:≥1050Mpa
Rockwell Hardness ≥85.5HRA
Vickers Hardness Hv20: ≥1050Mpa
Fracture Toughness(KIC): ≥3.7MPa.m1/2
Bending strength: ≥220Mpa
Wear Volume:≤0.25cm3
Appearance: white |
Rubber Thickness:6mm Rubber:Natural
Tensile strength(TSB):≥15Mpa
Shore A Hardness: 50-60
Thermal conductivity.(normal temperature): 2w/m·k
Adhesive between tile and rubber: 3.8Mpa
Elongation: 468%
Resilience:0.65 |
Steel Thickness: 6mm
Steel: Q235A or Q235B Q235A: C 0.14-0.22%
Mn 0.30-0.65% Si≤0.30 S≤0.050 P≤0.045 Q235B:
C 0.12-0.20% Mn 0.30-0.670% Si≤0.30 S≤0.045 P≤0.045 |
The rubber ceramic liner is made of excellent hot vulcanized rubber processing technology. The square or hemispherical wear-resistant ceramic liner and the vulcanized rubber are combined to produce a porcelain-vulcanized rubber composite wear-resistant ceramic vulcanized rubber sandwich panel.
The rubber ceramic liner combines the high toughness of porcelain with the high buffering and fatigue-relieving characteristics of vulcanized rubber, which can effectively solve the problem of anti-corrosion of machinery and equipment during the whole process of mass and boring transportation. It combines the high toughness of porcelain with the advantages of high buffering and fatigue relief of vulcanized rubber, which can effectively solve the problem of anti-corrosion of machinery and equipment during the whole process of mass and uninteresting transportation.
Also named wear ceramic parts, wear rubber ceramic plate, wear-resistant ceramic pads.
Ceramic rubber composite pads&plate is the use of rubber vulcanization process, to embed the wear-resistant ceramic vulcanized into rubber, stick it on the inner all of the equipment with the adhesive paste. As customers' requirements, it also can be vulcanized together with steel plate, with bolts or not.
Features:
It combines wear-resistance of ceramic and impact-resistance of rubber, apply to convey systems equipment work under normal temperature, and can bear some impact.
Applications:
Pipes and tanks
Deflectors
Launders
Spill Face Sloping Walls&Loading Chutes
Bins&Hoppers
Mill feed components
Detailed Photos
Mineral Processing equipment operates in some of the harshest and remote locations. It is crucial to the Mineral Processing industries that this equipment continues to operate efficiently and its lifecycle is maximized to minimize downtime. By appropriately protecting equipment from the extreme wear caused by the high speed and flow rates of ore when processed as a slurry ensures better equipment longevity. The slurry is highly abrasive and can not only cause wear damage to wet processing equipment but also with the inclusion of chemicals and heat, there is a constant risk of corrosion and dangerous leakage.
Wear Protection ceramic Linings are used throughout Mineral Processing to protect the steel surfaces of equipment from wear and corrosion. They are used on a range of equipment including pipes, tanks, chutes, pumps, flotation cells, thickeners, launders, and feed spouts or chutes.