| Standard: | JIS, GB, DIN, BS, ASTM, AISI |
|---|---|
| Application: | Metallurgical Machinery, Cement Plant, Mining Machine, Coal Yard |
| Material: | Aluminum |
| Type: | Wear Resistant Ceramic |
| Color: | White |
| Al2O3: | 92/95/99 |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier |
Industrial ceramic linings are a great option for guarding against abrasion, erosion or corrosion. However, ceramic linings are only effective when they are selected and installed properly. Monolithic shapes and custom engineered integrated tile systems can be provided for pieces with irregular geometries (such as elbows, tees and lateral wyes) where standard tiles are not cost-effective. Engineered solutions like these ensure an exact fit and 100% ceramic protection. |
||
| 92 Alumina Ceramic Liners | 95 Alumina Ceramic Liners | T95 Alumina Ceramic Liners |
| Al2O3:≥92% Density:≥3.6g/cm³ Porosity:<0.1% compressive strength:≥1050Mpa Rockwell Hardness ≥82HRA Vickers Hardness Hv20: ≥1050Mpa Fracture Toughness(KIC): ≥3.7MPa.m1/2 Bending strength: ≥220Mpa Wear Volume:≤0.25cm3 Appearance: white |
Al2O3:≥95% Density:≥3.65g/cm³ Porosity:<0.1% compressive strength:≥1300Mpa Rockwell Hardness ≥85HRA Vickers Hardness Hv20: ≥1100Mpa Fracture Toughness(KIC): ≥3.8MPa.m1/2 Bending strength: ≥250Mpa Wear Volume:≤0.20cm3 Appearance: white |
Al2O3:≥95% Density:≥3.70g/cm³ Porosity:<0.1% compressive strength:≥1600Mpa Rockwell Hardness ≥88HRA Vickers Hardness Hv20: ≥1150Mpa Fracture Toughness(KIC): ≥4.0MPa.m1/2 Bending strength: ≥300Mpa Wear Volume:≤0.15cm3 Appearance: white |
| 92 | 95 | T95 | 99 | ZTA | ZrO2 | Test Standard | |
| Density(g/cm³) | ≥3.6 | ≥3.65 | ≥3.7 | ≥3.83 | ≥4.15 | ≥5.9 | GB/T 25995-2010 |
| Al2O3(%) | ≥92% | ≥95% | ≥95% | ≥99% | ≥75% | / | JC/T 1085-2008 |
| ZrO2 +Y2O3 | / | / | / | / | ≥21% | ≥99.8% | JC/T 1085-2008 |
| Bending Strength(MPa) | ≥220 | ≥250 | ≥300 | ≥330 | ≥400 | ≥800 | GB/T 6569-2006 |
| Compressive Strength (MPa) | ≥1050 | ≥1300 | ≥1600 | ≥1800 | ≥2000 | / | GB/T 8489-2006 |
| Fracture Toughness(MPa.m1/2) | ≥3.2 | ≥3.2 | ≥3.5 | ≥3.5 | ≥5.0 | ≥7.0 | ISO21618 IM |
| Rockwell Hardness HRA | ≥82 | ≥85 | ≥88 | ≥89 | ≥90 | ≥88 | GB/T 230.1-1996 |
| Vickers Hardness HV20(MPa) | ≥950 | ≥1000 | ≥1100 | ≥1200 | ≥1400 | ≥1100 | GB/T 16534-2009 |
| Wear Volume(cm³) | ≤0.25 | ≤0.20 | ≤0.15 | ≤0.10 | ≤0.05 | ≤0.05 | JC/T2345-2015 |
Q: Are you a trading company or manufacturer?
1.Established in 1997,25 years experience in wear solutions products.
2.Factory is under expanding, the total construction area is 50,000 sqm.
3.ISO9001:2015 certified,over350 staffs.
4.Three Own-designed production lines, the ball mils are own produced.
We supply a wide range of pre-engineered alumina ceramic tiles tailor-made to suit any type of application such as short and long radius small and large bore pipes and pipe bends, square to round transitions, cones etc. The company also supply and install a range of pump impellers, expeller rings, and valves.
QMX provides wear resistant solutions to all industries including Mining, Mineral , Base & Precious Metal Smelting, Power Generation (coal fired power stations), Iron and Steel, Cement & Lime Manufacture, and Petro-Chemical Refining and Production.
Ceramic Liner: plain ceramic liner, weldable ceramic liner, trapezoidal ceramic liner, ceramic cylinder, ceramic block, alumina wear liner, rubber backed ceramic panel, ceramic composite panel, mining wear liner and so on.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}