| Standard: | GB |
|---|---|
| Application: | Loader, Metallurgical Machinery, Cement Plant, Mining Machine |
| Material: | Aluminum |
| Type: | Wear Resistant Ceramic |
| Density: | 3.60-4.2 |
| Al2O3 Content: | 92%, 95%, 99%, Zta |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier QMX offers several wear lining solutions especially developed to fit specific applications like truck beds, washing drums, concrete mixers and screen feed boxes. The solutions are developed to meet all your needs in terms of keeping material flow up and maintenance time down.
QMX wear plates minimize surface friction to prevent material from sticking. Excellent solution for bins, chutes, silos and other low wear applications. Suitable for applications that require extremely low friction.
| 92 | 95 | T95 | 99 | ZTA | ZrO2 | Test Standard | |
| Density(g/cm³) | ≥3.6 | ≥3.65 | ≥3.7 | ≥3.83 | ≥4.15 | ≥5.9 | GB/T 25995-2010 |
| Al2O3(%) | ≥92% | ≥95% | ≥95% | ≥99% | ≥75% | / | JC/T 1085-2008 |
| ZrO2 +Y2O3 | / | / | / | / | ≥21% | ≥99.8% | JC/T 1085-2008 |
| Bending Strength(MPa) | ≥220 | ≥250 | ≥300 | ≥330 | ≥400 | ≥800 | GB/T 6569-2006 |
| Compressive Strength (MPa) | ≥1050 | ≥1300 | ≥1600 | ≥1800 | ≥2000 | / | GB/T 8489-2006 |
| Fracture Toughness(MPa.m1/2) | ≥3.2 | ≥3.2 | ≥3.5 | ≥3.5 | ≥5.0 | ≥7.0 | ISO21618 IM |
| Rockwell Hardness HRA | ≥82 | ≥85 | ≥88 | ≥89 | ≥90 | ≥88 | GB/T 230.1-1996 |
| Vickers Hardness HV20(MPa) | ≥950 | ≥1000 | ≥1100 | ≥1200 | ≥1400 | ≥1100 | GB/T 16534-2009 |
| Wear Volume(cm³) | ≤0.25 | ≤0.20 | ≤0.15 | ≤0.10 | ≤0.05 | ≤0.05 | JC/T2345-2015 |