Wear resistant panel is compounded by rubber sheet, flat or spherical tiles and steel plate through hot vulcanizing process. It is fixed to equipment surface by means of bolts connection or adhesive. There are two types of ceramic surface,: flat and spherical. Wear resistant panel is high wearable, high cut-resistant, and super impact wear resistance. It is magically suitable under condition of systems conveying lower burning point materials, and outstanding feature of powerful impact.
Series of wear resistant panel
· Rubber alumina ceramic panel
· Ceramic pulley lagging
· Two-In-one wear resistant/composite panel with CN layer
· ZTA wear resistant panel
· Polyurethane wear resistant panel
· Silicon carbide wear resistant panel
for Vulcanized Panel
|
||
92 Alumina Ceramic Liners | WEAR PLATE BACKING MATERIALS | Mild Steel Backing Plate |
Al2O3:≥92% Density:≥3.6g/cm³ Porosity:<0.25 compressive strength:≥1050Mpa Rockwell Hardness ≥85.5HRA Vickers Hardness Hv20: ≥1050Mpa Fracture Toughness(KIC): ≥3.7MPa.m1/2 Bending strength: ≥220Mpa Wear Volume:≤0.25cm3 Appearance: white |
Rubber:Natural Tensile strength(TSB):≥15Mpa Shore A Hardness: 55-60 Thermal conductivity.(normal temperature): 2w/m·k Adhesive between Ceramic and rubber: 3.8Mpa Elongation: 468% Resilience:0.65 |
Steel: Q235A or Q235B Q235A: C 0.14-0.22% Mn 0.30-0.65% Si≤0.30 S≤0.050 P≤0.045 Q235B: C 0.12-0.20% Mn 0.30-0.670% Si≤0.30 S≤0.045 P≤0.045 |